Product description
Graphite-base coated electrode depositing pure nickel metal, recommended for assembling and repairing gray cast irons and repairing cracks. Homogeneous, machinable deposit, good filler metal adhesion and spreading.
Applications: Repairs to engine blocks, machine tool frames, gearboxes, reduction gears, pump bodies, castings, valve bodies.
Product application instructions
|
Grey, malleable, nodular cast irons: |
||||
|
NF A 32-101 |
: |
FGL 150, 200, 250, 300, 350, 400 |
||
|
NF A 32-201 |
: |
FGS 370-17, 400-12, 500-7, 600-3, 700-2 |
||
|
NF A 32-702 |
: |
MN 350-10, 380-18, 450-6, 350-4, 650-3 |
||
|
DIN 1691 |
: |
CG-14, 18, 25, 30 |
||
|
DIN 1693 |
: |
GGG-40, 50, 60, 70 |
||
|
DIN 1692 |
: |
GTS-35, 45, 55, 65, 70 |
||
Keep the heat input between passes as low as possible (max. 70°C) to minimize the risk of base metal cracking (weld with minimum intensity and lay short, narrow beads). To limit internal stresses in the base metal, we recommend hammering the weld bead after each pass (essential for flanged parts). Weld on clean, grease-free surfaces (grind joint beforehand).
= + –
~40V
Classification
| NF A 81-342 | AWS A 5.15 | DIN 8573 | EN ISO 1071 |
|---|---|---|---|
| E Ni BG 11 | E Ni-CI | E Ni BG 11 | E C Ni-CI 3 |
Chemical analysis (%)
| C | Mn | If | Fe | Ni |
|---|---|---|---|---|
| 1.2 | <1.0 | <2.0 | <2.0 | >95.0 |
Mechanical characteristics
| Rm (MPa) | Hardness |
|---|---|
| >300 | approx. 180 HB |
Why choose this basic electrode?
Vacuum-packed 5 or 6Kg electrode for welding highly stressed steel assemblies (carbon and carbon manganese) (tensile strength up to 510 MPa).
It features excellent mechanical properties, particularly at low temperatures.