FCW BNC-O
Rechargement anti-abrasion
Description du produit
• Tubular wire for self-shielded metal arc hardfacing
• Alloy designed for extreme resistance to high stress grinding abrasion with moderate impact
• The abrasion resistance and hardness are achieved in one layer thus allowing interesting cost saving
• Suitable for service temperatures up to 650°C
Instructions d'application du produit
APPLICATIONS
The deposit resists abrasion by small particles under high restraint or erosion in gaseous media.
Examples
Periphery and leading flight on ceramic augers, blast furnace bells and screens operating at high temperature, agglomeration fans, sinter stars, sinter exhausters etc.
Positions de soudage: Flat, half up, half down
Résistance à l'usure
Abrasion
Impact
Metal-Metal
Corrosion
Temperature
Classification
| EN 14700 |
|---|
| T ZFe3 |
Analyse chimique (%)
| C | Mn | Si | Cr | Nb | B | Fe |
|---|---|---|---|---|---|---|
| 2.5 | 2.0 | 0.6 | 11.5 | 5.0 | 2.2 | Rest |
Caractéristiques mécaniques
| Hardness – 3-Layer deposit as welded |
|---|
| 64-68 HRc |
Pourquoi choisir ce fil fourré?
- Résistance maximale à l’abrasion sèche et intense
Dépôt très riche en carbures de bore, niobium et chrome → très grande dureté et excellent comportement face aux matériaux très abrasifs.
- Dureté exceptionnelle du dépôt
Le dépôt atteint des duretés de > 63 HRC, offrant une longévité maximale même dans des environnements très sévères.
- Parfait pour les conditions sans chocs
Idéal là où l’usure est abrasive mais sans impact important (le dépôt est très dur mais peu tenace).
- Dépôt non usinable mais très résistant
Après soudage, le métal est seulement meulable, donc à réserver pour les zones d’usure pure.
- Très bon rendement
Apport contrôlé, fusion régulière, taux de déposition élevé → gain de temps et de productivité.