FCW 420S
Fil fourré pour le rechargement dur à l’arc submergé
Description du produit
• Tubular wire for submerged arc hardfacing
• 13% chromium martensitic stainless steel deposit
• Attractive combination of corrosion, oxidation, scaling and wear resistance
Instructions d'application du produit
APPLICATION
FCW 420S is used for hardfacing and reclaiming components subject to moderate corrosion and metal-metal wear. The deposited alloy also has excellent gouging and abrasion resistant properties.
Examples Extensively used as a cladding alloy on many types of steel industry rolling mill rolls such as table rolls, pinch rolls, scale breaker rolls, coiler rolls, leveller rolls and runout table rolls. Other applications include dragline rope sheaves, dragline rope drums, hydraulic plungers, certain types of valve seats, pulp rotors.
Position de soudage: A plat
Résistance à l'usure
Metal-Metal
Corrosion
Temperature
Impact
Abrasion
Classification
| EN 14700 |
|---|
| T Fe8 |
Analyse chimique (%)
| C | Mn | Si | Cr | Fe |
|---|---|---|---|---|
| 0.3 | 1.0 | 1.0 | 13.0 | Rest |
Caractéristiques mécaniques
| Hardness – 3-Layer deposit |
|---|
| 50 HRc |
Pourquoi choisir ce fil fourré ?
- Résistance élevée à l’abrasion et à la corrosion
Ce fil dépose un alliage à base de martensite inoxydable, équivalent au 420 (acier inox à 12–14 % Cr), offrant :
-une bonne dureté (~50–55 HRC) après refroidissement à l’air,
-une bonne résistance à l’abrasion, notamment par particules dures,
-une protection contre la corrosion légère à modérée.
- Dépôt dur, sans traitement thermique nécessaire
Le FCW 420-S forme une structure martensitique directement après soudage, ce qui évite un revenu thermique ou une trempe supplémentaire. Il est donc rapide à mettre en œuvre en rechargement.