Description du produit
• Rutile flux cored stainless steel wire for gas shielded arc welding
• 20% chromium – 10% nickel – 3% molybdenum deposit
• Attractive bead appearance, very good penetration and high productivity
• Excellent X-ray soundness
• Specifically designed for out-of-position welding
• Maximum productivity for completion of vertical welds
• Welded with classical economical Ar-CO2 mixtures or CO2
Instructions d'application du produit
APPLICATIONS
FCW V 20 9 3 offers a strong, tough crack free deposit suitable for tank and other military vehicle fabrication. It is also useful for welding high tensile steels, for joining 13% manganese steels and more generally as a multi-purpose wire for maintenance and for welding dissimilar joints.
4A, MVEE816
Positions de soudage
EN ISO 6947:PA, PB, PC, PD, PE, PF, PG
ASME IX:1F, 1G, 2F, 2G, 3F, 3G, 4F, 4G, 5G
Classification
| AWS A 5.22 | EN ISO 17633-A |
|---|---|
| E308MoT1-1/4 | T 20 10 3 P M 1 - T 20 10 3 P C 1 |
Analyse chimique (%)
| C | Mn | Si | Cr | Ni | Mo |
|---|---|---|---|---|---|
| 0.050 | 1.50 | 0.80 | 20.5 | 9.70 | 2.90 |
Caractéristiques mécaniques
| Rm (MPa) | Rp0.2 (MPa) | A5 (%) | KCV (J) |
|---|---|---|---|
| 750 | 520 | 30 | 20°C : 60 |
Pourquoi choisir cette électrode basique?
Electrode en emballage sous vide de 5 ou 6Kg pour le soudage des assemblages en acier (carbone et carbone manganèse) fortement sollicités (résistance à la traction jusqu’à 510 MPa).
Elle se caractérise par d’excellentes propriétés mécaniques, en particulier aux basses températures.